| OSU 001 |
| |
Composition: |
Zn 99.99 |
| |
Coating hardness: |
25 HV0.3 |
| |
Melting point: |
420 °C (788 °F) |
| |
Post treatment: |
Painting |
| |
Properties: |
Corrosion protection |
| |
|
|
| OSU 002 |
| |
Composition: |
85Zn 15Al |
| |
Coating hardness: |
35 HV0.3 |
| |
Melting point: |
450 °C (842 °F) |
| |
Post treatment: |
Painting |
| |
Properties: |
Corrosion protection in industrial and
marine atmospheres, high resistance in SO2-laden atmospheres |
| |
|
|
| OSU 004 |
| |
Composition: |
Al 99.5 |
| |
Coating hardness: |
40 HV0.3 |
| |
Melting point: |
660 °C (1220 °F) |
| |
Post treatment: |
Painting |
| |
Properties |
Corrosion protection in industrial and
marine atmospheres, scale-resisting surface up to 800°C on steel through
formation of a diffusion zone. Coatings in the food processing industry. |
| |
|
|
| OSU 006 |
| |
Composition: |
Al 5Mg |
| |
Coating hardness: |
40 HV0.3 |
| |
Melting point: |
630 °C (1166 °F) |
| |
Post treatment: |
Painting |
| |
Properties: |
Very good corrosion protection in
seawater and weakly alkaline solutions uses in offshore installations |
| |
|
|
| OSU 009 |
| |
Composition: |
Zn 99+ |
| |
Coating hardness: |
40-80 HV0.3 |
| |
Melting point: |
390 °C (734 °F) |
| |
Post treatment: |
--- |
| |
Properties: |
Zinc alloys for mould-making |
| |
|
|
| OSU 010 |
| |
Composition: |
Ni-based alloy |
| |
Coating hardness: |
120 HV0.3 |
| |
Melting point: |
1450 °C (2642 °F) |
| |
Post treatment: |
Turning |
| |
Properties: |
Undercoat suitable for arc spraying
for ceramic and steel coatings, corrosion-resistant in alkaline solutions |
| |
|
|
| OSU 030 |
| |
Composition: |
Steel (8Mn 2Si) |
| |
Coating hardness: |
200-300 HV0.3 |
| |
Melting point: |
1510 °C (2750 °F) |
| |
Post treatment: |
Turning |
| |
Properties: |
Medium-hard, turnable steel coating
for repair and maintenance |
| |
|
|
| OSU 060 |
| |
Composition: |
X46 Steel (13Cr) |
| |
Coating hardness: |
350-550 HV0.3 |
| |
Melting point: |
1480 °C (2696 °F) |
| |
Post treatment: |
Turning / grinding |
| |
Properties: |
13% chromium steel. Hard, wear-resistant, low-corrosion
steel coating, most commonly used as a wire metallizing coating for wear
protection |
| |
|
|
| OSU 062 |
| |
Composition: |
X35 Steel (17Cr Mo) |
| |
Coating hardness: |
350-550 HV0.3 |
| |
Melting point: |
1480 °C (2696 °F) |
| |
Post treatment: |
Turning / grinding |
| |
Properties: |
17% chromium steel. Hard,
wear-resistant, low-corrosion steel coating |
| |
|
|
| OSU 065 |
| |
Composition: |
110 Mn Cr Ti 8 |
| |
Coating hardness: |
300-500 HV0.3 |
| |
Melting point: |
1460 °C (2660 °F) |
| |
Post treatment: |
Grinding |
| |
Properties: |
Hard, wear-resistant carbon steel
coating |
| |
|
|
| OSU 085 |
| |
Composition: |
X15 Steel (18Cr 8Ni 7Mn) |
| |
Coating hardness: |
170-280 HV0.3 |
| |
Melting point: |
1510 °C (2750 °F) |
| |
Post treatment: |
Turning |
|
Properties: |
High alloy chrome-nickel-manganese
steel. Easily machined, low-corrosion, resistant to abrasion |
|
|
|
| OSU 095 |
|
Composition: |
X5 Steel (17Cr 12Ni 2Mo) |
|
Coating hardness: |
170-300 HV0.3 |
| |
Melting point: |
1510 °C (2750 °F) |
| |
Post treatment: |
Turning |
| |
Properties: |
Easily machined, low-corrosion high
alloy chrome- nickel-steel coating |
| |
|
|
| OSU 096 |
| |
Composition: |
25Cr 5Al |
| |
Coating hardness: |
180-250 HV0.3 |
| |
Melting point: |
1500 °C (2732 °F) |
| |
Post treatment: |
Turning |
| |
Properties: |
High alloy chrome-aluminum steel.
Very good bonding, scale-resistant, corrosion-resistant in sulfurous media
up to 900°C (1650 °F) |
| |
|
|
| OSU 100 |
| |
Composition: |
Mo 99.95 |
| |
Coating hardness: |
200-600 HV0.3 |
| |
Melting point: |
2650 °C (4802 °F) |
| |
Post treatment: |
Grinding |
| |
Properties: |
Very good bonding on aluminum and
copper |
| |
|
|
| OSU 110 |
| |
Composition: |
Cu 99.9 |
| |
Coating hardness: |
60-150 HV0.3 |
| |
Melting point: |
1080 °C (1976 °F) |
| |
Post treatment: |
Turning |
| |
Properties: |
Good electrical and thermal
conductivity, coatings can be polished |
| |
|
|
| OSU 120 |
| |
Composition: |
Cu 37Zn |
| |
Coating hardness: |
70 HV0.3 |
| |
Melting point: |
920 °C (1688 °F) |
| |
Post treatment: |
Turning |
| |
Properties: |
For decorative brass coatings |
| |
|
|
| OSU 130 |
| |
Composition: |
Cu 7Sn |
| |
Coating hardness |
120-200 HV0.3: |
| |
Melting point: |
1040 °C (1904 °F) |
| |
Post treatment: |
Turning |
| |
Properties: |
Hard, wear-resistant tin bronze, good
running qualities |
| |
|
|
| OSU 142 |
| |
Composition: |
Cu 8Al |
| |
Coating hardness: |
120-200 HV0.3 |
| |
Melting point: |
1035 °C (1895 °F) |
| |
Post treatment: |
Turning |
| |
Properties: |
Very good bonding; hard,
wear-resistant aluminum-bronze for heavily stressed bearings |
| |
|
|
| OSU 150 |
| |
Composition: |
Ni 99.2 |
| |
Coating hardness: |
80-180 HV0.3 |
| |
Melting point: |
1455 °C (2651 °F) |
| |
Post treatment: |
Turning |
| |
Properties: |
Good bonding, protects against
corrosion by alkaline media |
| |
|
|
| OSU 151 |
| |
Composition: |
64Ni 32Cu |
| |
Coating hardness: |
140-200 HV0.3 |
| |
Melting point: |
1340 °C (2444 °F) |
| |
Post treatment: |
Turning |
| |
Properties: |
Monel material with
corrosion resistance in seawater, excellent machinability, good running
qualities |
| |
|
|
| OSU 160 |
| |
Composition: |
80Ni 20Cr |
| |
Coating hardness: |
140-250 HV0.3 |
| |
Melting point: |
1395 °C (2543 °F) |
| |
Post treatment: |
Turning |
| |
Properties: |
Very good bonding, scale-resisting
undercoat and buffer coat for ceramics; corrosion- resistant, easily
machined coating |
| |
|
|
| OSU 170 |
| |
Composition: |
Sn 99.9 |
| |
Coating hardness: |
15-25 HV0.3 |
| |
Melting point: |
232 °C (450 °F) |
| |
Post treatment: |
--- |
| |
Properties: |
Anti-corrosion coatings in the food
industry, solderable coatings |
| |
|
|
| OSU 171 |
| |
Composition: |
Sn 7Sb 4Cu |
| |
Coating hardness: |
20 HV0.3 |
| |
Melting point: |
265 °C (509 °F) |
| |
Post treatment: |
Turning |
| |
Properties: |
Bearing metal, tin-based |